Universal stainless offers this alloy and a wide.
13 8 stainless steel hardness.
13 8 mo is an age hardening stainless steel with high strength and hardness along with good levels of resistance to both general corrosion and stress corrosion cracking.
13 8 stainless steel round bar per ams 5629 can be heat treated to h1000 per ams 2759 3.
The principal features of type 13 8 are good resistance to general and stress corrosion cracking and high strength that is developed by a single low temperature heat treatment.
Alloy 13 8 stainless is a martensitic precipitation hardening stainless steel that has excellent strength high hardness superior toughness and good corrosion resistance.
This alloy is double melted in a vacuum induction furnace followed by consumable electrode vacuum melt vim var.
13 8 stainless is a martensitic precipitation hardening stainless steel that has excellent strength high hardness superior toughness and good corrosion resistance.
The addition of molybdenum allows improved pitting resistance as compared to other precipitation hardened grades such as 15 5 and 17 4.
Uns s13800 capable of astm a564 centerless ground bar.
In condition h 950 ph 13 8 mo stainless has rusting resistance similar to that of type 304 stainless in 5 weight percent salt fog.
13 8 stainless alloy uns s13800 is a martensitic precipitation hardening stainless steel that has excellent strength high hardness superior toughness and good corrosion resistance.
This alloy offers good corrosion resistance and excellent strength.
Good transverse toughness properties are achieved by tight chemical composition control low carbon content and vacuum melting.
Ph 13 8 mo has been used for aircraft components nuclear reactor components valve parts fittings landing gear parts and pins.
In strongly oxidizing and reducing acids and in atmospheric exposures the general corrosion resistance of ph 13 8 mo stainless approaches that of type 304.
Or in some cases 2nd melt is by electroslag remelting esr as specified by the consumer.
Type 13 8 is a martensitic precipitation age hardenable stainless steel.
13 8 uns s13800.
13 8 stainless steel flat bar per ams 5629 can be heat treated to h1000 per ams 2759 3 dms 2100.
Ati 13 8 alloy uns s13800 is a martensitic precipitation hardening stainless steel that has excellent strength high hardness superior toughness and good corrosion resistance.
Compared to other ferrous base materials alloy 13 8 stainless steel offers a high level of useful mechanical properties under severe environmental conditions.
Good transverse toughness properties are achieved by tight chemical composition control low carbon content and vacuum melting.
13 8 stainless steel plate per ams 5629 astm a 564 693 ams 5864.
13 8 is a precipitation hardened martensitic stainless steel alloy that is melted as vim var.